- Products
- Polyurethane Resin Product Series
- Polyurethane for Fabric Lamination
Fabric and Film Lamination
Applied to lamination for PU film-to-fabric, fabric-to-fabric, PU film-to PU film, PVC sheet-to-fabric and PVC sheet-to-tarpaulin fabric, good for wet adhesion or semi-dry adhesion processing.
Applicable for
+ Luggage
+ Medical bed
+ Water bags
+ Oil bags
+ Furniture
+ Fabrics
+ Bedding
+ Industrial fabrics
PRODUCT DESCRIPTION
- Hard or soft, high or low solid content, high strength, good wash resistance, without organic Tin
- After reacting with cross-linking agent, it can produce high strength and high toughness effect.
APPLICATION TO END-USE PRODUCTS
- Two-component PU, applied to lamination for PU film-to-fabric, fabric-to-fabric, PU film-to PU film, PVC sheet-to-fabric and PVC sheet-to-tarpaulin fabric, good for wet adhesion or semi-dry adhesion processing.
- Applicable for in the luggage, medical bed, water bags, oil bags, furniture, fabrics, bedding and industrial fabrics, etc.
PRODUCTS
ADD InquiryINQUIRY | Item No. | Solid Content (N.V.) (%) | Viscosity (Vis.) (CPS/25℃) | Modulus, 100% (Kgf/cm²) | Solvents | Tensile Strength (Kgf/cm²) | Elongation at Break (%) |
Characteristics |
---|---|---|---|---|---|---|---|---|
NC-5050K | 67±3 | 25000-50000 | 15±3 | MEK | 200-250 | 400-600 | Toluene free, for TPU film-to-fabric, fabric-to-fabric | |
NC-5060K | 60±2 | 70000-90000 | 15±5 | MEK | 150-300 | 300-500 | Toluene free, for TPU film-to-fabric, fabric-to-fabric | |
NC-5060KE | 60±2 | 50000-100000 | 15±5 | MEK/EAC | 150-300 | 300-500 | Soft, viscous, washable and excellent in adhesion | |
NC-5060T | 60±2 | 75000-95000 | 15±5 | DMF/MEK/TOL | 150-300 | 300-500 | For PU film-to-fabric, fabric-to-fabric | |
NC-5070K | 70±2.5 | 30000-50000 | 15±3 | MEK | 200-250 | 400-600 | Toluene free, for TPU film-to-fabric, fabric-to-fabric | |
CX-2550H | 38±3 | 1300-2000 | 50±10 | EAC | >150 | >400 | Soft, hydrolysis resistance, great bonding strength | |
CX-6029H | 38±1.5 | 8000-13000 | 35±5 | DMF/MEK/TOL | >300 | >800 | One-component PU, soft, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
CX-6030K | 16±2 | 1000-4000 | 92.5±7.5 | MEK | >200 | >500 | Round table on glue for PVC tape and T/C, T/R, non-woven cloth and then mesh, early and high strength | |
CX-6030KE | 30±1 | 1000-1500 | 92.5±7.5 | MEK/EAC | 200-300 | >500 | High initial strength | |
CX-6030KM | 30±1 | 1000-1500 | 92.5±7.5 | MEK/EAC | 200-300 | >500 | Roller coating, excellent adhesion in initial process, for PVC sheet-to-tarpaulin fabric | |
CX-6030KMB | 30±1 | 1000-1500 | 92.5±7.5 | DMF/EAC/DMC | >200 | >500 | Toluene free, soft, great bonding strength | |
CX-6030DE | 30±1 | 1000-1500 | 92.5±7.5 | EAC/DMC | 200-300 | >500 | Roller coating, excellent adhesion in initial process, for PVC tape-to-T/C, T/R, non-woven and mesh fabric | |
CX-6030KS | 30±1 | 1000-1500 | 55±5 | MEK/EAC/DMC | >200 | >500 | Soft, gear coating, laminating for PVC sheet and tarpaulin, high initial adhesion | |
CX-6032 | 30±1 | 2000-5000 | 92.5±7.5 | DMF/MEK | >200 | >500 | Roller coating, excellent adhesion in initial process, for PVC sheet-to-tarpaulin fabric | |
CX-6035H | 33±1 | 80000-120000 | 15±3 (cross-linking agent 5%) |
DMF/MEK/TOL/EAC | 200-300 | >500 | Two-component PU, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
CX-6040 | 30±1 | 4000-7000 | 50±5 | DMF/MEK/TOL | >300 | >700 | One-component PU, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
CX-6041 | 30±1 | 4000-7000 | 50±5 | MEK/TOL | >300 | >700 | One-component PU, high adhesion and good fluidity at high temperature | |
CX-6045 | 45±1.5 | 10000-15000 | 15±3 (cross-linking agent 5%) |
DMF/MEK/TOL | 170-220 | 400-600 | Soft, roller coating, for PU film-to-fabric | |
CX-6045A | 45±1.5 | 10000-15000 | 15±3 (cross-linking agent 5%) |
DMF/MEK/TOL/EAC | >150 | 400-600 | Soft, roller coating, for PU film-to-fabric | |
CX-6045AU | 45±1.5 | 10000-15000 | 15±3 (cross-linking agent 5%) |
DMF/MEK/TOL/EAC | >150 | 400-600 | Soft, high viscosity, good adhesion, for film-to-fabric and fabric-to-fabric | |
CX-6045AH | 45±1.5 | 30000-40000 | 15±3 (cross-linking agent 5%) |
DMF/MEK/TOL/EAC | >150 | 400-600 | Soft, knife coating, for PU film-to-fabric | |
CX-6045H | 45±1.5 | 50000-90000 | 15±3 | DMF/MEK/TOL | 170-220 | 400-600 | Soft, knife coating, for PU film-to-fabric | |
CX-6049U | 30±1.5 | 5000-10000 | 35±5 | DMF/MEK/TOL | >300 | >800 | High adhesion, good elasticity and low melting point | |
CX-6065K | 35±1.5 | 80000-140000 | 40±5 | DMF/DMC/EAC | >300 | >600 | Medium hard grade, knife coating, for PVC sheet-to-fabric | |
CX-6065F | 35±1.5 | 80000-140000 | 40±5 | DMF/TOL/DMC | >300 | >600 | Medium hard grade, knife coating, for PVC sheet-to-fabric | |
CX-6152 | 27±1 | 30000-60000 | 52.5±2.5 | DMF/TOL | 400-500 | 700-900 | Knife coating, for PU film-to-fabric and PVC sheet-to-fabric | |
CX-6152K | 27±1 | 30000-60000 | 55±5 | DEF/MEK/DMC | >400 | >700 | Knife coating, for PU film-to-fabric and PVC sheet-to-fabric | |
CX-6335F | 35±1.5 | 80000-140000 | 40±5 | MEK/TOL | >300 | >600 | Medium hard grade, knife coating, for PVC sheet-to-fabric | |
CX-6400M | 35±1 | 3000-6000 | 45±5 | MEK/TOL | 300-400 | 500-600 | Medium hard grade, roller coating, for PVC sheet-to-fabric | |
CX-6400JM | 30±1.5 | 30000-60000 | 52.5±7.5 | DMF/TOL | >300 | >500 | High initial strength | |
CX-6400L | 30±1 | 3000-6000 | 45±5 | MEK/TOL | 300-400 | 500-600 | Hard | |
CX-6800H | 35±1 | 60000-100000 | 37.5±2.5 | DMF/MEK/TOL | 400-500 | 600-700 | High initial strength, soft | |
CX-6800HND | 35±1.5 | 60000-100000 | 130±30 | DEF/MEK/TOL/EAC | 300-700 | 300-500 | High initial strength, soft, DMF Free | |
CX-6950D | 50±1.5 | 60000-100000 | 30±5 | DMF/MEK/TOL | 600-700 | 300-400 | Soft, knife coating, seawater resistant, for PU film-to-fabric and PVC sheet-to-fabric |
REMARKS
- Please contact us for other products which are not on this brochure.
- The above data are just for general reference and could not be used as guarantee document.