Reactive polyurethane Hot-melt Adhesives (PUR), its chemical structure of the NCO functional groups, and the moisture in the air crosslinking reaction, the formation of a great molecular weight of PU structure.
Solid at room temperature before use must be put to the oven or other heating equipment to a certain processing temperature (about 80-150 ℃), then the processing, so-called reactive hot melt adhesives.
PRODUCT DESCRIPTION
- Long operation time, fast curing speed, soft after curing, low temperature operation and high initial adhesion. After curing process, the bonding result shows high strength and toughness.
APPLICATION TO END-USE PRODUCTS
- Applicable for lamination of TPU films, fabric to fabric, PVC sheets, PU sheets and fabric base lamination. Widely used in all kinds of clothing, light bags, bags & cases, medical products, water bladders, inflated beds and industrial fabrics, etc.
PRODUCTS
ADD InquiryINQUIRY | Item No. | Appearance | Viscosity (Vis.) (CPS/25℃) |
Modulus, 100% (Kgf/cm²) |
Tensile Strength (Kgf/cm²) |
Elongation at Break (%) |
Characteristic/ Application |
Suggested Processing Temperature (℃) |
---|---|---|---|---|---|---|---|---|
PR-6801 | Gray-white solid | 14000±3000 (120℃) | 40-60 | >200 | >400 | Excellent edge bonding strength, fast curing speed, high tack & good adhesion. Applicable for wooden floor and hook and loop lamination. | 100-140 | |
PR-6801K | Gray-white solid | 14000±3000 (120℃) | 35-40 | 100-150 | 1100-1300 | Fast curing speed, high initial adhesion. Applicable for hook and loop lamination. | 100-130 | |
PR-6803 | Paste | 8000±2000 (100℃) | 26-29 | 150-250 | 250-650 | Long open time, very soft after curing. Applicable for textile bonding and hook//loop lamination. | 90-110 |
REMARKS
- Please contact us for other products which are not on this brochure.
- The above data are just for general reference and could not be used as guarantee document.