Reactive polyurethane Hot-melt Adhesives (PUR), its chemical structure of the NCO functional groups, and the moisture in the air crosslinking reaction, the formation of a great molecular weight of PU structure.
Solid at room temperature before use must be put to the oven or other heating equipment to a certain processing temperature (about 80-150 ℃), then the processing, so-called reactive hot melt adhesives.
PRODUCT DESCRIPTION
- Long operation time, fast curing speed, soft after curing, low temperature operation and high initial adhesion. After curing process, the bonding result shows high strength and toughness.
APPLICATION TO END-USE PRODUCTS
- Applicable for lamination of TPU films, fabric to fabric, PVC sheets, PU sheets and fabric base lamination. Widely used in all kinds of clothing, light bags, bags & cases, medical products, water bladders, inflated beds and industrial fabrics, etc.
PRODUCTS
ADD InquiryINQUIRY | Item No. | Appearance | Viscosity (Vis.) (CPS) | Modulus, 100% (Kgf/cm²) |
Tensile Strength (Kgf/cm²) |
Elongation at Break (%) |
Characteristic/ Application | Suggested Processing Temperature (℃) |
---|---|---|---|---|---|---|---|---|
PR-6226 | Paste | 8000±2000 (100℃) | 26-29 | 150-250 | 250-650 | Long open time, high green strength, very soft after curing, application for the lamination of fabric and fabric. | 90-110 | |
PR-6226F | Paste | 8000±2000 (100℃) | 26-29 | 150-250 | 250-650 | Long open time, high green strength, very soft after curing, application for the lamination of fabric and fabric. | 90-110 | |
PR-6507 | Light Yellow, solid | 10000±2000 (100℃) | 25-30 | 250-300 | 400-600 | For fabric and TPU film lamination | 90-110 | |
PR-6508 | Paste | 6000±2000 (100℃) | 14-18 | 120-200 | 450-650 | Water repellent type for fabric and TPU film lamination | 90-110 | |
PR-6510FR | Paste | 8000±2000 (100℃) | 100-130 | 170-200 | 320-380 | Long open time, flame retardancy, high green strength, Anti-UV agent | 90-110 | |
PR-6511 | Clear yellow paste | 13000±2000 (100℃) | 28-38 | 450-550 | 650-750 | Long open time, very soft after cured, high green strength | 90-110 | |
PR-6590EH | Light yellow paste | 6000-10000 (120℃) | 30-60 | >300 | >700 | Long operation time, rapid curing, soft hand after ripening, good continuity | 100-120 |
REMARKS
- Please contact us for other products which are not on this brochure.
- The above data are just for general reference and could not be used as guarantee document.