- Products
- Polyurethane Resin Product Series
- Polyurethane for Fabric Lamination
Fabric and Fabric Lamination
Applied to lamination for PU film-to-fabric, fabric-to-fabric, PU film-to PU film, PVC sheet-to-fabric and PVC sheet-to-tarpaulin fabric, good for wet adhesion or semi-dry adhesion processing.
Applicable for
+ Luggage
+ Medical bed
+ Water bags
+ Oil bags
+ Furniture
+ Fabrics
+ Bedding
+ Industrial fabrics
PRODUCT DESCRIPTION
- Hard or soft, high or low solid content, high strength, good wash resistance, without organic Tin
- After reacting with cross-linking agent, it can produce high strength and high toughness effect.
APPLICATION TO END-USE PRODUCTS
- Two-component PU, applied to lamination for PU film-to-fabric, fabric-to-fabric, PU film-to PU film, PVC sheet-to-fabric and PVC sheet-to-tarpaulin fabric, good for wet adhesion or semi-dry adhesion processing.
- Applicable for in the luggage, medical bed, water bags, oil bags, furniture, fabrics, bedding and industrial fabrics, etc.
PRODUCTS
ADD Inquiry| INQUIRY | Item No. | Solid Content (N.V.) (%) | Viscosity (Vis.) (CPS/25℃) | Modulus, 100% (Kgf/cm²) | Solvents | Tensile Strength (Kgf/cm²) | Elongation at Break (%) |
Characteristics |
|---|---|---|---|---|---|---|---|---|
| AD-2060 | 60±2 | 60000-110000 | 20±5 | DMF/MEK/TOL | 150-300 | 300-500 | Semi-dry lamination process, hydrolysis resistance, good flexibility at low temperature | |
| CX-6029H | 38±1.5 | 8000-13000 | 35±5 | DMF/MEK/TOL | >300 | >800 | One-component PU, soft, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
| CX-6035H | 33±1 | 80000-120000 | 15±3 (cross-linking agent 5%) |
DMF/MEK/TOL/EAC | 200-300 | >500 | Two-component PU, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
| CX-6040 | 30±1 | 4000-7000 | 50±5 | DMF/MEK/TOL | >300 | >700 | One-component PU, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
| CX-6041 | 30±1 | 4000-7000 | 50±5 | MEK/TOL | >300 | >700 | One-component PU, high adhesion and good fluidity at high temperature | |
| CX-6080 | 40±1 | 10000-20000 | 35±5 | DMF/MEK/TOL/EAC | >200 | >500 | One-component hot-melt adhesives, soft and high elasticity | |
| CX-6085 | 40±1 | 15000-20000 | 50±10 | DMF/MEK/TOL | >200 | >500 | One-component hot-melt adhesives, low operating temperature | |
| NC-5050K | 67±3 | 25000-50000 | 15±3 | MEK | 200-250 | 400-600 | Toluene free, for TPU film-to-fabric, fabric-to-fabric | |
| NC-5060K | 60±2 | 70000-90000 | 15±5 | MEK | 150-300 | 300-500 | Toluene free, for TPU film-to-fabric, fabric-to-fabric | |
| NC-5060KE | 60±2 | 50000-100000 | 15±5 | MEK/EAC | 150-300 | 300-500 | Soft, viscous, washable and excellent in adhesion | |
| NC-5060T | 60±2 | 75000-95000 | 15±5 | DMF/MEK/TOL | 150-300 | 300-500 | For PU film-to-fabric, fabric-to-fabric | |
| NC-5060TH | 60±2 | 90000-115000 | 15±5 | DMF/MEK/TOL | 150-300 | 300-500 | For PU film-to-fabric, fabric-to-fabric, soft | |
| NC-5070K | 70±2.5 | 30000-50000 | 15±3 | MEK | 200-250 | 400-600 | Toluene free, for TPU film-to-fabric, fabric-to-fabric |
REMARKS
- Please contact us for other products which are not on this brochure.
- The above data are just for general reference and could not be used as guarantee document.