- Polyurethane for Fabric Lamination
Hot-melt Adhesive
Applied to lamination for PU film-to-fabric, fabric-to-fabric, PU film-to PU film, PVC sheet-to-fabric and PVC sheet-to-tarpaulin fabric, good for wet adhesion or semi-dry adhesion processing.
Applicable for
+ Luggage
+ Medical bed
+ Water bags
+ Oil bags
+ Furniture
+ Fabrics
+ Bedding
+ Industrial fabrics
PRODUCT DESCRIPTION
- Hard or soft, high or low solid content, high strength, good wash resistance, without organic Tin
- After reacting with cross-linking agent, it can produce high strength and high toughness effect.
APPLICATION TO END-USE PRODUCTS
- Two-component PU, applied to lamination for PU film-to-fabric, fabric-to-fabric, PU film-to PU film, PVC sheet-to-fabric and PVC sheet-to-tarpaulin fabric, good for wet adhesion or semi-dry adhesion processing.
- Applicable for in the luggage, medical bed, water bags, oil bags, furniture, fabrics, bedding and industrial fabrics, etc.
PRODUCTS
ADD Inquiry| INQUIRY | Item No. | Solid Content (N.V.) (%) | Viscosity (Vis.) (CPS/25℃) | Modulus, 100% (Kgf/cm²) | Solvents | Tensile Strength (Kgf/cm²) | Elongation at Break (%) |
Characteristics |
|---|---|---|---|---|---|---|---|---|
| CX-6029H | 38±1.5 | 8000-13000 | 35±5 | DMF/MEK/TOL | >300 | >800 | One-component PU, soft, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
| CX-6029HF | 37±1 | 9000-13000 | 35±5 | DMF/MEK/TOL | >300 | >800 | Soft, matte surface | |
| CX-6038 | 25±1 | 4000-7000 | 45±5 | DMF/MEK/TOL | >300 | >500 | One-component PU, high bonding strength | |
| CX-6038K | 38±1.5 | 15000-20000 | 45±5 | MEK | >300 | >500 | One-component PU, high bonding strength | |
| CX-6040 | 30±1 | 4000-7000 | 50±5 | DMF/MEK/TOL | >300 | >700 | One-component PU, for PU film-to-fabric, wet adhesion or semi-dry adhesion processing | |
| CX-6041 | 30±1 | 4000-7000 | 50±5 | MEK/TOL | >300 | >700 | One-component PU, high adhesion and good fluidity at high temperature | |
| CX-6049 | 30±1.5 | 5000-10000 | 35±5 | DMF/MEK/TOL | >300 | >800 | High adhesion, good elasticity and low melting point | |
| CX-6049ND | 30±1 | 6000-10000 | 35±5 | DEF/MEK/DMC | >300 | >800 | High adhesion, good elasticity and low melting point, DMF/TOL free | |
| CX-6080 | 40±1 | 10000-20000 | 35±5 | DMF/MEK/TOL/EAC | >200 | >500 | One-component hot-melt adhesives, soft and high elasticity | |
| CX-6085 | 40±1 | 15000-20000 | 50±10 | DMF/MEK/TOL | >200 | >500 | One-component hot-melt adhesives, low operating temperature | |
| CX-6636 | 20±2 | 3000-6000 | 80±10 | MEK/TOL | >200 | >400 | It can be used as hot-melt adhesive to laminate fabric and fabric | |
| CX-6800M | 40±2 | 3500-11500 | 25±5 | DMF/MEK | 150-250 | 700-900 | Excellent bonding strength for TPU, PVC, leather, fabric, etc. | |
| CX-6902 | 40 ± 1 | 2000-4000 | 55 | DMF/MEK/TOL | 90 | 500 | One-component PU adhesive with high adhesion, good elasticity and low melting point |
REMARKS
- Please contact us for other products which are not on this brochure.
- The above data are just for general reference and could not be used as guarantee document.